Evaluation of surface roughness of the bracket slot floor—a 3D perspective study

Progress in Orthodontics volume 17, Article number: 3 (2016) Cite this article

Abstract

Background

An important constituent of an orthodontic appliance is orthodontic brackets. It is either the bracket or the archwire that slides through the bracket slot, during sliding mechanics. Overcoming the friction between the two surfaces demands an important consideration in an appliance design. The present study investigated the surface roughness of four different commercially available stainless steel brackets.

Methods

All tests were carried out to analyse quantitatively the morphological surface of the bracket slot floor with the help of scanning electron microscope (SEM) machine and to qualitatively analyse the average surface roughness (Sa) of the bracket slot floor with the help of a three-dimensional (3D) non-contact optical surface profilometer machine.

Results

The SEM microphotographs were evaluated with the help of visual analogue scale, the surface roughness for group A = 0—very rough surface, group C = 1—rough surface, group B = 2—smooth surface, and group D = 3—very smooth surface. Surface roughness evaluation with the 3D non-contact optical surface profilometer machine was highest for group A, followed by group C, group B and group D. Groups B and D provided smooth surface roughness; however, group D had the very smooth surface with values 0.74 and 0.75 for mesial and distal slots, respectively.

Conclusions

Evaluation of surface roughness of the bracket slot floor with both SEM and profilometer machine led to the conclusion that the average surface roughness was highest for group A, followed by group C, group B and group D.

Background

One of the important constituents of an orthodontic appliance is brackets. Brackets stay for more time in the patient’s mouth, among all orthodontic materials [1]. In fixed orthodontic treatment, some degree of sliding between bracket and archwire occurs and the frictional resistance is encountered. So between the two surfaces, overcoming the friction demands an important consideration in an appliance design [2].

The frictional force to the force with which the contacting surfaces are pressed together is proportional and is affected by the nature of the surface at the interface (rough or smooth, chemically reactive or passive, modified by lubricants, etc.). This is because all surfaces, however smooth they are, have irregularities which are seen as large on a molecular scale, and real contact occurs at the peaks of the surface irregularities. These peaks, known as asperities, between the two surfaces carry the entire load [3, 4].

As compared to aesthetic ceramic brackets, metal brackets of stainless steel have a good superficial surface homogeneity and because of which, it has favourable mechanical properties and corrosion resistance. Even though a protective passive layer is present on the SS alloy, the Fe, Cr, or Ni (or all) ions may still be released from the metal surface in the acidic oral environment over the corrosion processes, which increases the risk of tissue damage, aesthetic changes (staining of the tooth by corrosive products) and loss of metal properties [5, 6].

Between bracket-wire interfaces, the friction occurs. Some force which is applied is dissipated as friction, and the remainder is being transferred to the supporting structures of the tooth to initiate tooth movement. So if the applied force is of sufficient magnitude, there is an occurrence of biological tooth response [4]. Hence, the amount of friction has a direct relation with the accuracy of bracket slot dimension and bracket slot roughness. This tempted us to evaluate the surface roughness of the bracket slot floor.

The ongoing appliance evolution resulted in two orthodontic bracket sizes that a clinician may choose either 0.018- or 0.022-in. slot. The 0.022-in.-slot size is larger as compared to 0.018-in. slot and facilitates easier wire insertion and less frictional binding during initial alignment and provides increased stiffness during retraction. McLaughlin, Bennett and Trevisi (MBT) itself recommends using 0.022-in. slot and also most of the orthodontists prefer using this slot size, so we decided to use 0.022-in. slot brackets for the study.

Hence, the present in vitro study was conducted to evaluate the surface roughness in three dimensions of the stainless steel bracket slot which can help to determine the clinical performance of the bracket, the accuracy of bracket slot dimension and roughness of the bracket slot.

Aim and objectives

To access and compare the surface roughness of various as-received commercially available conventional 0.022 in. (0.56 mm) slot, MBT prescribed upper right 1st premolar stainless steel brackets.

Methods

A total of 80 pre-adjusted conventional upper right first premolar stainless steel brackets in as-received condition with 0.022 in. (0.56 mm) slot and with MBT prescription (0° tip, −7° torque) from four different manufacturers were taken. In a sample size of 80 brackets, 20 brackets were allotted in each group as

  • Group A: Gemini, 3M Unitek (Monrovia, CA)

  • Group B: Mini 2000, Ormco Corp. (Glendora, CA)

  • Group C: Opti-MIM, Ortho Organizers (San Marcos, CA)

  • Group D: Mini master, American Orthodontics (Sheboygan, WI)

The following apparatus were used for the study:

  • Scanning electron microscope (SEM) machine (JSM-6360A, JEOL, Japan, available at Pune, India, with 10–20 kV) (Fig. 1)

    Fig. 1
    figure 1

    Scanning electron microscope (SEM) machine

    Full size image

  • Three-dimensional (3D) non-contact optical surface profilometer machine (Taylor Hobson, England, available at Bangalore, India) (Fig. 2)

    Fig. 2
    figure 2

    3D surface profilometer machine (Taylor Hobson)

    Full size image

Procedure for scanning electron microscopy

From the sample of as-received 80 brackets, 20 brackets—i.e. 5 brackets from each group (groups A, B, C, and D) were randomly selected to analyse the morphological surface of the bracket slot floor (mesial and distal slots), with the help of a SEM machine (Fig. 1). The surface was scanned and viewed on the monitor screen and representative microphotographs at ×5000 magnification [5] of each bracket slot floor were obtained, which was sufficient to have a clear view of the surface characteristics of the slot floor area (Fig. 3). The images which were obtained were saved for the visual evaluation, using a discrete scale quantitative classification containing four scores [6, 7]:

Fig. 3
figure 3

SEM microphotographs of stainless steel bracket slot from different manufacturers (×5000 magnification): a 3M Unitek, b Ormco, c Ortho Organizers, and d American Orthodontics

Full size image

  • 0—very rough surface

  • 1—rough surface

  • 2—smooth surface

  • 3—very smooth surface

Surface roughness measurement

Each group was evaluated for the Sa of the bracket slot floor with the help of a 3D non-contact optical surface profilometer machine (Fig. 2).

The measurements were done in sequence of the group’s name like group A was evaluated first then group B, C and D, respectively. Also, each time measurement of the mesial slot was done first and then the distal slot for all the samples to maintain a standardized protocol. Each sample was placed on the flat surface of the profilometer machine with the help of a tweezer, under the beam of the white light interferometry which is usually made up of the He-Ne, 633 nm [8].

Configuration settings

Scanning speed

The ×1 option was selected, such that the slower the scanning speed of the sample, the greater will be the details of the fringes of the bracket slot floor as shown in Fig. 4.

Fig. 4
figure 4

a Stainless steel bracket, b bracket view under the three-dimensional profiler machine, c distal slot view of the bracket, and d distal slot view of the bracket after scanning showing the scanned slot surface

Full size image

Measurement setting

The measurement of the slot surface roughness is analysed by software Digital Surf, (TalyMap Platinum software, Leicester, England. Version no. 6.1.6001), from which we can receive 3D and 2D surface texture parameters (Fig. 5). The 3D surface texture parameters and height parameters (ISO25178) are the following (Fig. 6d):

Fig. 5
figure 5

Measurement settings

Full size image
Fig. 6
figure 6

Steps in recording the 3D surface texture parameters. a Raw surface view, b levelled surface. c Threshold applied. d. Surface parameters

Full size image

  • Sp—maximum peak height

  • Sv—maximum pit height

  • Sz—maximum height

  • Sq—root mean square height

  • Ssk—skewness

  • Sku—kurtosis

  • Sa—arithmetic mean height

From these 3D parameters, we are interested in the Sa value which is an average of the surface heights giving us the average surface roughness of the bracket slot floor in three dimensions.

From the point of two-dimensional parameters, Ra value is of significant importance as it is the mean of the roughness profile. But the Ra value represents the slot in two dimensions. If we draw several lines (profile lines) on the area of the bracket slot floor, we will receive several readings for a single slot of the bracket, which means each bracket slot will have many different Ra values, which is not the case in the three-dimensional Sa value, as it is the average of the whole surface area, the area as a whole which is taken into consideration (rectangular dotted line Fig. 7d).

Fig. 7
figure 7

Showing images of the bracket slot. a–c The profile lines indicate average roughness (Ra) which is two-dimensional. d The marked rectangular area as a whole indicates the average surface roughness (Sa) which is three-dimensional

Full size image

A template is made (Fig. 6) in which once the slot surface is scanned, a raw surface view of the slot is received. The raw surface view which was obtained requires a levelling to be done, so that the whole surface is levelled in one form with the help of the software Digital Surf, (TalyMap Platinum software, Leicester, England, Version no. 6.1.6001). Once this is achieved and the threshold is applied, the software eliminates the highest peak and the deepest valley of the slot floor surface and gives the readings which are less biassed by these highest peak and the deepest valley.

An ICC test between examiners was performed. Twenty percent of the samples from each group were re-evaluated in order to evaluate the error of the method.

Likewise, all the 80 samples of stainless steel bracket measurements were completed. One hundred sixty readings of the Sa value were obtained (Table 3).

Table 1 One-way ANOVA test for slot surface roughness
Full size table
Table 2 Results of Tukey’s test for slot surface roughness
Full size table
Table 3 Average surface roughness (Sa values) of bracket slot (measurement in micrometre)
Full size table

Method of statistical analysis

  1. 1.

    SEM analysis—images were analysed, using a discrete scale quantitative classification containing four scores.

  2. 2.

    Surface roughness analysis—all the data collected had normal distribution, so we could apply the parametric tests. Analysis of variance (ANOVA) was used to determine whether the difference between the groups was significant or not.

  3. 3.

    Post hoc comparison test (Tukey’s multiple comparison test) was used for inter-group comparison.

Results

Scanning electron microscope results

Surface roughness scores were group A = 0—very rough surface, group C = 1—rough surface, group B = 2—smooth surface, and group D = 3—very smooth surface, respectively. This suggests that group D bracket slot floor were smoother as compared to group A, group B, and group C, respectively.

Surface roughness results

Figure 8 shows the mean of the Sa values across the four groups, the surface roughness for both mesial and distal slots was highest in group A, followed by C, B and D, respectively. This indicates that there were differences in the surface roughness across the four groups with group D having the smoothest surface with values 0.74 and 0.75 for the mesial and distal slots, respectively.

Fig. 8
figure 8

Average surface roughness (Sa) mean values in micrometre across the four groups

Full size image

Table 1 shows the results of the ANOVA test. From the results, we noticed that the F-statistic of the average surface roughness for the mesial slot was 6.898479 and for the distal it was 16.0508, both of these values result in a very low p value (<0.001) which allows us to reject the null hypothesis and conclude that a difference amongst the means across the four groups was present.

Table 2 shows the results of the Tukey’s multiple comparison test (post hoc test). Thus, surface roughness was highest for group A, followed by C, B and D, respectively. Groups B and D provided smooth surface roughness; however, group D had the very smooth surface with values 0.74 and 0.75 for the mesial and distal slots, respectively.

Discussion

Resistance to sliding (RS) between brackets and archwires during treatment greatly influences the force transmitted to the teeth; to close the extraction space, sliding mechanics are widely used, and they may reduce the orthodontic force as much as 50 % of the bracket [9] and archwire materials. The coefficient of friction is an important factor in RS [10, 11], which might depend on the roughness, texture, and/or hardness of the contacting material surfaces [12]. Thus, studies of bracket surface roughness are of great clinical interest.

Previous studies have measured the surface roughness of brackets and archwires using scanning electron microscopy [13, 14], a contact surface profilometer [15, 16] and atomic force microscopy [11, 15, 17–19] (AFM). SEM can visualize two dimensionally the surface morphology, and a quantitative information is not being provided regarding the selected area. A contact profilometer allows two-dimensional determination of surface roughness parameter values. However, the sample surface adjacent to the scanning line may be damaged as the measured area is in the form of a line, and in contrast, more advantages are being provided by AFM, such as 3D quantitative and configuration measurements of the selected surface. A 3D non-contact surface profilometer which is available and is based on white light interferometry methods uses He-Ne beam of 633 nm [8] which can successfully allow determination and 3D imaging of surface roughness parameter values. The measurement needs no sample preparation and is non-destructive. So, the test range cover of ∼10 mm can be achieved. So, the surface roughness of the all the specimens were evaluated by using SEM and 3D interferometry profilometer machines, which is non-destructive and much faster compared with a stylus profilometer, and with a larger field, needing no sample preparation, compared with AFM [6].

Hence, all the tests were carried out to analyse quantitatively the morphological surface of the bracket slot floor with the help of SEM machine and to qualitatively analyse the Sa of the bracket slot floor with the help of the 3D non-contact optical surface profilometer machine. In the present study, it was found that the F-statistic of average surface roughness for the mesial slot was 6.898479 and for the distal, it was 16.0508 both of these values result in a very low p value (<0.001) which concluded that a difference amongst the means across the four groups was present. The surface roughness was highest for group A, followed by C, B and D, respectively. Groups B and D provided smooth surface roughness; however, group D had the very smooth surface with values 0.74 and 0.75 for the mesial and distal slots, respectively.

Ceramic brackets, whether they are single crystal sapphire, polycrystalline alumina, or zirconia, relative to stainless steel (SS) brackets, have poor frictional properties [13, 20, 21]. To combat this, aesthetic ceramic brackets with metallic slot have been developed [22, 23]. Compared to stainless steel brackets, titanium brackets have more surface roughness [24, 25]. Self-ligating brackets [26–28] with low-friction and full bracket engagement of the archwire, which is easy to use, assist good oral hygiene and is comfortable for the patient. But because of its partially reduced torquing capacity and high cost, conventional brackets are widely being used [29]. The above studies reveal that conventional metallic brackets are widely used than ceramic, zirconia, titanium, and self-ligating brackets either due to their properties or cost factor. Hence, the present study evaluated the conventional stainless steel brackets.

The present study was conducted to analyse the Sa of the bracket slot floor of the conventional stainless steel bracket with the help of the 3D non-contact optical surface profilometer machine. The surface roughness was highest for group A, followed by C, B and D, respectively. Groups B and D provided smooth surface roughness; however, group D had the very smooth surface with values 0.74 and 0.75 for the mesial and distal slots, respectively.

In order to select the proper low-friction bracket system, clinicians should consider specific characteristics of slot design [30]. MBT recommends 0.022-in.-slot height than 0.018-in.-slot height [31]. Regarding the use of 0.022-in.-slot, 54 % of orthodontists preferred the 0.022-in.-slot size [32]. With this view, we decided to take 0.022-in. MBT slot conventional stainless steel brackets for the present study. Upper-right first premolar brackets were included in this study as to maintain a standardized protocol.

Many previous studies [1, 2, 6, 17, 19, 20, 24, 31–37] have been done on surface roughness. Some of these studies evaluated the friction characteristics, surface roughness, ligation method, etc. To evaluate friction, there is a need to compare any two materials like stainless steel, ceramic, either mono or polycrystalline, titanium, and zirconium. But the present study evaluated the surface roughness of stainless steel brackets itself with the help of the 3D non-contact optical surface profilometer machine and SEM. There was no comparison of friction of the stainless steel brackets with the other materials like wires or ligation technique. So the study was focussed on evaluating the surface roughness in three dimensions of the stainless steel bracket slot which can help to determine the clinical performance of the bracket, the accuracy of bracket slot dimension and bracket slot roughness. The brackets Mini 2000, Ormco Corp. (Glendora, CA) and Mini master (American Orthodontics) have smooth surfaces of bracket slot.

The effects of the oral environment cannot be simulated in an in vitro exploration, and a possible limitation of the present study is the small sample size in each group. In vivo studies with a large sample size in each group will be needed to examine the intraoral exposure effects on surface roughness in three dimensions of the stainless steel bracket slot.

Conclusions

  • On SEM evaluation for surface roughness of bracket slot floor, surface roughness for group D was found to be the smoothest of all the groups, while group B is less smooth, group C is rough, and group A was found to have a very rough surface.

  • Measurement of surface roughness of the bracket slot floor with the 3D non-contact surface profilometer machine, led to the conclusion that the average surface roughness was highest for group A, followed by group C, group B and group D, respectively.

References

  1. Liu X, Lin J, Ding P. Changes in the surface roughness and friction coefficient of orthodontic bracket slots before and after treatment. Scanning. 2013;35:265–72.

    Article  PubMed  Google Scholar 

  2. Doshi UH, Bhad Patil WA. Static frictional force and surface roughness of various bracket and wire combinations. Am J Orthod Dentofacial Orthop. 2011;139:74–9.

    Article  PubMed  Google Scholar 

  3. Proffit WR, Fields HW, Sarver DM. Contemporary orthodontics, 4th ed. St. Louis: Mosby; 2009. p. 377.

    Google Scholar 

  4. Nanda R. Biomechanics in clinical orthodontics. Philadelphia: WB Saunders Co; 1997. p. 190–96.

    Google Scholar 

  5. Juvvadi SR, Kailasam V, Padmanabhan S, Chitharanjan AB. Physical, mechanical, and flexural properties of 3 orthodontic wires: an in-vitro study. Am J Orthod Dentofacial Orthop. 2010;138:623–30.

    Article  PubMed  Google Scholar 

  6. Dolci GS, Spohr AM, Zimmer ER, Marchioro EM. Assessment of the dimensions and surface characteristics of orthodontic wires and bracket slots. Dental Press J Orthod. 2013;18:69–75.

    Article  PubMed  Google Scholar 

  7. Chappard D, Degasne I, Hure G, Legand E, Audan M, Basle MF. Image analysis of roughness by texture and fractal analysis correlate with contact profilometry. Biomater. 2003;24:1399–407.

    Article  Google Scholar 

  8. Synak R, Lipinski W, Pawelczak M. A novel method for areal surface roughness measurement. World Acad Sci Eng Tech. 2012;69:223–7.

    Google Scholar 

  9. Drescher D, Bourauel C, Schumacher H. Frictional forces between bracket and archwire. Am J Orthod Dentofacial Orthop. 1989;96:397–404.

    Article  PubMed  Google Scholar 

  10. De Franco DJ, Spiller RE, von Fraunhofer JA. Frictional resistance using Teflon-coated ligatures with various bracket-archwire combinations. Angle Orthod. 1995;65:63–74.

    PubMed  Google Scholar 

  11. Choi S, Park KH, Cheong Y, Kim HK, Park YG, Park HK. Changes in ultrastructure and properties of bracket slots after orthodontic treatment with bicuspid extraction. Scanning. 2011;33:25–32.

    Article  PubMed  Google Scholar 

  12. Loftus BP, Artun J, Nicholls JI, Alonzo TA, Stoner JA. Evaluation of friction during sliding tooth movement in various bracket-arch wire combinations. Am J Orthod Dentofacial Orthop. 1999;116:336–45.

    Article  PubMed  Google Scholar 

  13. Saunders CR, Kusy RP. Surface topography and frictional characteristics of ceramic brackets. Am J Orthod Dentofacial Orthop. 1994;106:76–87.

    Article  PubMed  Google Scholar 

  14. Marques IS, Araujo AM, Gurgel JA, Normando D. Debris, roughness and friction of stainless steel archwires following clinical use. Angle Orthod. 2010;80:521–7.

    Article  PubMed  Google Scholar 

  15. Bourauel C, Fries T, Drescher D, Plietsch R. Surface roughness of orthodontic wires via atomic force microscopy, laser specular reflectance, and profilometry. Eur J Orthod. 1998;20:79–92.

    Article  PubMed  Google Scholar 

  16. Zinelis S, Eliades T, Eliades G, Makou M, Silikas N. Comparative assessment of the roughness, hardness, and wear resistance of aesthetic bracket materials. Dent Mater. 2005;21:890–4.

    Article  PubMed  Google Scholar 

  17. Lin MC, Lin SC, Lee TH, Huang HH. Surface analysis and corrosion resistance of different stainless steel orthodontic brackets in artificial saliva. Angle Orthod. 2006;76:322–9.

    PubMed  Google Scholar 

  18. Alcock JP, Barbour ME, Sandy JR, Ireland AJ. Nano-indentation of orthodontic archwires: the effect of decontamination and clinical use on hardness, elastic modulus and surface roughness. Dent Mater. 2009;25:1039–43.

    Article  PubMed  Google Scholar 

  19. Lee GJ, Park KH, Park YG, Park HK. A quantitative AFM analysis of nano-scale surface roughness in various orthodontic brackets. Micron. 2010;41:775–82.

    Article  PubMed  Google Scholar 

  20. Pratten DH, Popli K, Germane N, Gunsolley JC. Frictional resistance of ceramic and stainless steel orthodontic brackets. Am J Orthod Dentofacial Orthop. 1990;98:398–403.

    Article  PubMed  Google Scholar 

  21. Keith O, Kusy RP, Whitley JQ. Zirconia brackets: an evaluation of morphology and coefficients of friction. Am J Orthod Dentofacial Orthop. 1994;106:605–14.

    Article  PubMed  Google Scholar 

  22. Angolkar PV, Kapila S, Duncanson MG, Nanda RS. Evaluation of friction between ceramic brackets and orthodontic wires of four alloys. Am J Orthod Dentofacial Orthop. 1990;98:499–506.

    PubMed  Google Scholar 

  23. Ghafari J. Problems associated with ceramic brackets suggest limiting use on selected teeth. Angle Orthod. 1992;62:145–52.

    PubMed  Google Scholar 

  24. Kusy RP, Whitely JQ, Ambrose WW, Newman JG. Evaluation of titanium brackets for orthodontic treatment: part I. The passive configuration. Am J Orthod Dentofacial Orthop. 1998;114:558–72.

    Article  PubMed  Google Scholar 

  25. Kusy RP, O’Grady PW. Evaluation of titanium brackets for orthodontic treatment: part II. The active configuration. Am J Orthod Dentofacial Orthop. 2000;118:675–84.

    Article  PubMed  Google Scholar 

  26. Kusy RP, Whitely JQ. Effects of sliding velocity on coefficients of friction in a model orthodontic system. Dent Mater. 1989;5:235–40.

    Article  PubMed  Google Scholar 

  27. Birnie D, Harradine N. Self-ligating orthodontic brackets. Semin Orthod. 2008;14:1–100.

    Article  Google Scholar 

  28. Hain M, Dhopatkar A, Rock P. A comparison of different ligation methods on friction. Am J Orthod Dentofacial Orthop. 2006;130:666–70.

    Article  PubMed  Google Scholar 

  29. Cacciafesta V, Sfondrini MF, Ricciardi A, Scribante A, Klersy C, Auricchio F. Evaluation of friction of stainless steel and esthetic self-ligating brackets in various bracket-archwire combinations. Am J Orthod Dentofacial Orthop. 2003;124:395–402.

    Article  PubMed  Google Scholar 

  30. Nucera R, Giudice LA, Matarese G, Artemisia A, Bramanti E, Crupi P, et al. Analysis of the characteristics of slot design affecting resistance to sliding during active archwire configurations. Prog in Orthod. 2013;14:35.

    Article  Google Scholar 

  31. McLaughlin RP, Bennett JC, Trevisi HJ. Systemized orthodontic treatment mechanics. St Louis, Mo: Mosby; 2002. p. 13–4.

    Google Scholar 

  32. Lombardo L, Wierusz W, Toscano D, Lapenta R, Kaplan A, Siciliani G. Frictional resistance exerted by different lingual and labial brackets: an in vitro study. Prog in Orthod. 2013;14:37.

    Article  Google Scholar 

  33. Keim RG, Gottlieb EL, Nelson AH, Vogel DS. 2002 JCO study of orthodontic diagnosis and treatment procedures: part 1: results and trends. J Clin Orthod. 2002;36:553–68.

    PubMed  Google Scholar 

  34. Subbiah S, Balasubramanian RK, Raj PK, Dilip S. Comparison of frictional resistance between conventional stainless steel, metal insert ceramic, self-ligating stainless steel and self ligating ceramic brackets with stainless steel wire: in vitro study. J Ind Orthod Soc. 2010;44:58–62.

    Google Scholar 

  35. Faizee KMSH, Thomas S, Krishnaswamy NR. Frictional characteristics of active and passive self-ligation bracket systems: an in vitro study. J Ind Orthod Soc. 2011;45:154–9.

    Article  Google Scholar 

  36. Galvão BM, Camporesi M, Tortamano A, Dominguez GC, Defraia E. Frictional resistance in monocrystalline ceramic brackets with conventional and nonconventional elastomeric ligatures. Prog in Orthod. 2013;14:9.

    Article  Google Scholar 

  37. Choi SH, Kang DY, Hwang CJ. Surface roughness of three types of modern plastic bracket slot floors and frictional resistance. Angle Orthod. 2014;84:177–83.

    Article  PubMed  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Pune, Maharashtra, India

    Chetankumar O. Agarwal

  2. Department of Orthodontics, S.M.B.T. Dental College and Hospital, Sangamner, Maharashtra, India

    Ketan K. Vakil, Avinash Mahamuni, Prasad V. Gayake & Jeegar K. Vakil

  3. Department of Orthodontics, Dr. Rajesh Ramdasji Kambe Dental College and Hospital, Akola, Maharashtra, India

    Pawankumar Dnyandeo Tekale

Authors
  1. Chetankumar O. Agarwal
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Ketan K. Vakil
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Avinash Mahamuni
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Pawankumar Dnyandeo Tekale
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Prasad V. Gayake
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Jeegar K. Vakil
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Chetankumar O. Agarwal.

Additional information

Competing interests

The authors declare that they have no competing interests.

Authors’ contribution

The work presented here was carried out in teamwork amongst all authors. COA and KKV designed the research protocol and design of the study. COA has taken the SEM images of the brackets and made the 3D measurements for each brackets. AM and PVG had performed the analysis of data. KKV, PVG and PDT had contributed to the conception of the study. PDT drafted the manuscript and KKV had given final approval of the version to be published. PDT and JKV had revised the manuscript for important intellectual contents. All authors read and approved the final manuscript.

Rights and permissions

Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Agarwal, C.O., Vakil, K.K., Mahamuni, A. et al. Evaluation of surface roughness of the bracket slot floor—a 3D perspective study. Prog Orthod. 17, 3 (2016). https://doi.org/10.1186/s40510-016-0116-2

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1186/s40510-016-0116-2

Keywords